Seamless carbon steel pipe hardness test method

Inner diameter of seamless steel pipe is more than 6.0mm and wall thickness is less than 13mm annealed seamless steel pipe material, which can be used W-B75 Webster Hardness test with very fast, easy, suitable for rapid non-destructive of the seamless steel pipe material qualified inspection. Inner diameter of seamless steel pipe is greater than 30mm and wall thickness greater than 1.2mm seamless steel tubes, using a Rockwell hardness test HRB, HRC hardness.

Inner diameter of seamless steel pipe is greater than 30mm, wall thickness less than 1.2mm of seamless steel tubes, Rockwell superficial hardness test hardness of HRT or HRN. Diameter less than 0mm, more than 4.8mm of seamless steel pipe, pipe dedicated Rockwell hardness test HR15T hardness. When the seamless steel pipe inner diameter greater than 26mm, you can also use the Rockwell or the Rockwell superficial hardness test hardness of the pipe wall.

The tensile test uses carbon steel pipes made of samples, sample in the tensile test machine will pull to fracture, then the determination of one or several mechanical properties, usually only the determination of tensile strength, yield strength, percentage elongation and section shrinkage. The tensile test the mechanical properties of metal materials, the basic test methods, almost all metallic materials, as long as the mechanical properties required to provide a tensile test. Especially those who shape is not easy material hardness test, tensile test to become only the mechanical properties testing means. The hardness test is a hard indenter prescribed conditions slowly pressed into the surface of the sample, and then test the indentation depth or size, in order to determine the size of the material hardness. The hardness test is the mechanical performance test with the easiest, fastest and most easy to implement. Hardness test is non-destructive, the approximate conversion relationship between hardness and tensile strength values. The material's hardness value can be converted into the tensile strength values, it has great practical significance.

Tensile test is not easy to test the strength is very convenient, so people are increasingly test hardness and less test its strength, and hardness conversion. Hardness manufacturing technology continues to progress and innovation, the original can not directly test the hardness of materials, such as seamless steel pipe, stainless steel plate and stainless steel bands, now may directly test the hardness of the Therefore, there is a hardness test is gradually replaced by the trend of the tensile test. The hardness test of the stainless steel to take into account its mechanical properties, performance and quality of this is related to the deformation of stainless steel as raw materials, stamping, cutting and other processing. Therefore, all seamless steel tubes for mechanical properties testing. Mechanical properties of the test method is mainly divided into two categories, a tensile test, hardness test.

Most of which are national standards in stainless steel also provides the tensile test and hardness test. For those not easy for hardness testing of materials, such as seamless steel pipe only requires that the tensile test. Stainless steel standard, general provisions of the cloth, Luo, Victoria three hardness test method, determination of the HB, HRB (HRC) and the HV hardness value, the provisions of the three hardness values ​​only for one can be. Especially the newly developed portable superficial Rockwell hardness tester, pipe Rockwell hardness tester can be as thin as 0.05mm stainless steel plate, stainless steel with a thin to 4.8mm seamless steel tubes for fast, accurate hardness testing, making difficult to resolve domestic problems solved.



Tech & Service of Seamless pipe

Seamless pipes are extensively applied for the nuclear device, gas, petrochemical, ship building and boiler industries. Seamless pipes dominates 65% of market share in Chinese boiler industry.

How to make seamless pipe(seamless pipe process)?
Hot Piercing Workshop
Piercing process
The cross roll piercing and pilger rolling process in the size range from approx. 250 to 660 mm outside diameter.
Precision cold drawn steel tube production process
Pipe weld cracks
often follow different mechanisms can be divided into two types of thermal cracking and cold cracking.
How to calculate a steel pipe and tube theoretic weight
Calculate a steel pipe?
Pipe fittings are necessary to join together pipes, or to change the direction of an existing pipe.
Pipe beveling
Pipe beveling is the process where an angle is formed between the edge of the end of a pipe or tube and a plane perpendicular to the surface.
Steel pipe cutting machine
Pipe cutting
Cutting tools have a grinding wheel piece cutting machine (also known as toothless saw), hand saw, cutter and other hand tools.
Packing the steel pipes
There are probably hundreds of different methods for packing a pipe, and most of them have merit, but there are two principles that are vital for any method.


SUNNY STEEL

Our team are highly trained and experienced in servicing and producing all types of steel supplies. Whether you've got a large construction project, or need parts for industrial machinery, our team of steel fabrication consultants will ensure that your project is provided with the parts you need, when you need them.

Link exchange

Copyright © 2011 Sunny Steel Enterprise Ltd.  All Rights Reserved ICP No.:08010763